You are describing "dry" annealing there. This has not been applied anywhere, as it requires removing and reinstalling the internal support structures inside the reactor vessel.
A somewhat lower temperature "wet" annealing process has been applied to two test reactors. I don't think it's been applied to any full scale power reactors.